Thermabond Medical Fleece (3 metres)
Termobond Medical Fleece is a non-woven fabric which consists ofthreelayers of 100% Polypropylene + 100 polyamide + 100% polyester, it is mainy used to make disposable face masks or filters for cotton masks.
!!! This material does not protect against Covid-19 !!!
Composition:PES, PP, PA
Width: 180cm
Weight:30 gsm
OEKO-TEX Certificate:IW00023IW Class 100
The item is sold by 3 metres in separate cuts, so if you order 6m, you'll receive x2 3m cuts.
Technical data:
Product thickness: 0.37 +/- 0.17 mm (PN-EN ISO 9073/2: 2002)
Strength along: min 40 N / 5cm (PN-EN 29073-3: 1994 I = 100mm)
Strength in width: min 8 N / 5cm (PN-EN 29073-3: 1994 I = 100mm)
Elongation along: min 25% (PN-EN 29073-3: 1994 I = 100mm)
Elongation across: min 45% (PN-EN 29073-3: 1994 I = 100mm)
Technological process:
Thermobonded nonwovens are obtained by using the temperature and pressure of calender rollers. The nonwoven fleece undergoes the calendering process, i.e. simultaneous pressure + temperature. We obtain a product with very low thickness, good stackability and adequate strength.
Original: $3.00
-70%$3.00
$0.90Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
Termobond Medical Fleece is a non-woven fabric which consists ofthreelayers of 100% Polypropylene + 100 polyamide + 100% polyester, it is mainy used to make disposable face masks or filters for cotton masks.
!!! This material does not protect against Covid-19 !!!
Composition:PES, PP, PA
Width: 180cm
Weight:30 gsm
OEKO-TEX Certificate:IW00023IW Class 100
The item is sold by 3 metres in separate cuts, so if you order 6m, you'll receive x2 3m cuts.
Technical data:
Product thickness: 0.37 +/- 0.17 mm (PN-EN ISO 9073/2: 2002)
Strength along: min 40 N / 5cm (PN-EN 29073-3: 1994 I = 100mm)
Strength in width: min 8 N / 5cm (PN-EN 29073-3: 1994 I = 100mm)
Elongation along: min 25% (PN-EN 29073-3: 1994 I = 100mm)
Elongation across: min 45% (PN-EN 29073-3: 1994 I = 100mm)
Technological process:
Thermobonded nonwovens are obtained by using the temperature and pressure of calender rollers. The nonwoven fleece undergoes the calendering process, i.e. simultaneous pressure + temperature. We obtain a product with very low thickness, good stackability and adequate strength.